M-2 High Speed Steel
BLUE STREAK AISI M-2 HIGH SPEED STEEL
Flats - Rounds - Squares - Hollowbar
Standard Sizes - Non-Standard Sizes - Metric Sizes
Very high red hardness.
High hardening response.
Outstanding wear resistance.
|
TREATMENT
|
TEMPERATURE RANGE
|
COOLING/QUENCHING
|
NOTES
|
|
FORGING
|
1975-2075° F
|
Slow.
|
Do not forge below 1700° F. Anneal after forging.
|
|
ANNEALING
|
1550-1600° F
|
Cool slowly at a rate of 35° F per hour to 1000° F.
|
For best results, insulating media is desirable. Hold at temperature for 2
hours.
|
|
STRESS RELIEVING
|
1100-1300° F
|
Cool slowly
|
Stress relieve after rough machining
|
|
PREHEATING
|
1500-1550° F
|
|
Preheat time in furnace is ¾ Hr. per inch of thickness. Heating up
to temperature as slow as possible.
|
|
HARDENING
|
2225-2275° F (furnace)
2200-2225° F (salt bath)
|
Quench in air or warm oil. To minimize quenching strains, quench in salt at
1000° F
|
For maximum wear resistance, harden at 2275° F. For maximum toughness
and high hardness, harden at 2200° F.
|
|
TEMPERING
|
(See Chart)
|
|
Double tempering is required. The usual tempering time is 2+2 hours.
Recommended temperature is 1000-1075° F.
|
Data is typical and should not be construed as actual values for any catagory.
Applications and technical information require engineers and tool designers to exercise