Click to learn more about Diehl Tool Steel's Diehl Express rapid tool steel turnaround
 
Accu-Square Logo

Diehl Tool Steel has been selling quality tool steel for over 85 years

Diehl Tool Steel is an ISO 9001:2008 certified company

1-800-543-1566

Request a tool steel quote from Diehl Tool Steel
Email Diehl Tool Steel Customer Service

1-800-543-1566

Request a quote from Diehl Tool SteelEmail Diehl Tool Steel Customer Service

Print this pageEmail this to someoneShare on LinkedInShare on Google+Share on Facebook

CPM 10V

CPM 10V® Powder Metal

CPM 10V® powder metal tool steel is a versatile air hardening tool and die steel which provides extremely high wear resistance in combination with relatively high impact toughness. A very large volume of hard vanadium carbides provides the high wear resistance. The good impact toughness is the result of the fine grain size, small carbides, and superior cleanliness of the powder metallurgy (CPM®) microstructure. CPM 10V® offers substantially better wear resistance than the high carbon, high chromium die steels such as D-2 and D-7.

Analysis:


C

CO

CR

MN

MO

NI

P

S

SI

V

W
2.455.251.309.75

Size Availability:

Flats • Hollowbar • Metric • Non-Standard • Rounds • Squares • Standard

Applications:

Blanking DiesCold Extrusion PunchesForming Dies
Piercing DiesPlastic Mold DiesPunches
Shear BladesSlitting CuttersTrimming Dies

Data is typical and should not be construed as actual values for any category.
Applications and technical information require engineers and tool designers to exercise independent judgement.

CPM 10V HEAT TREATING INSRUCTIONS

Hardening

Preheating:

1500-1550°F, equalize.

Critical Temperature:

Acl: 1540°F

Austenitizing (High Heat):

Heat rapidly from the preheat, typically by transferring to a second furnace.

For Optimum Wear Resistance:

Soak for 5 to 15 minutes; Furnace or Salt Bath: 2150°F;

For Balance of Wear Resistance & Toughness:

Soak for 15 to 30 minutes; Furnace or Salt Bath: 2050°F

For Maximum Toughness & Minimum Distortion in Cooling:

Soak for 30 to 60 minutes; Furnace: 1975°F; Salt Bath: 1950°F

Quenching:

Air pressurized gas warm oil or salt. Sections less than 3″ thick may be air cooled to maximum hardness. Sections 3″ thick or more must be quenched at a faster rate using one of the methods below to attain maximum hardness.
For pressurized gas, the furnace should have a minimum quench pressure of 4 bars. The quench rate to below 1000 °F is critical to obtain the desired properties. For oil, quench until black, about 900°F, then cool in still air to 150-125°F. For salt, maintained at 1000-1100°F, equalize in the salt, then cool in still air to 150-125°F.

As Oil Quenched fromHRC
1950°F, 45 minutes65
2050°F, 20 minutes65
2100°F, 15 minutes64
2150°F, 5 minutes63

Tempering:Temper immediately after quenching. Typical temperature range is 1000-1100°F. Do not temper below 1000°F. Hold at temperature for 2 hours then air cool to ambient temperature. Double tempering is required. Triple tempering is required when austenitized at 2100°F or higher.

Oil Quenched from 1950°F, 45 minutes
Tempering Temp °FHRC
100060
105056.5
110051
115046

 

Oil Quenched from 2050°F, 20 minutes
Tempering Temp °FHRC
100063
105060.5
110055
115050
115045

 

Oil Quenched from 2150°F, 5 minutes
Tempering Temp °FHRC
100064
105061
110056
115051
115046

Annealing

Annealing must be performed after hot working and before re-hardening. Heat at a rate not exceeding 400°F per hour to 1600-1650°F and hold at temperature for 1 hour per inch of maximum thickness; 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 50°F per hour to 1000°F. Continue cooling to ambient temperature in the furnace or in air. The resultant hardness should be a maximum of 277 HB. The data presented herein are typical values and do not warrant suitability for any specific application or use of this material. Normal variations in the chemical composition, the size of the product, and heat treatment parameters may result in different values for the various physical and mechanical properties .

Print this pageEmail this to someoneShare on LinkedInShare on Google+Share on Facebook
Request Mailed Literature
Enter your name and address and we will mail you our latest brochures and information sheets.
  • This field is for validation purposes and should be left unchanged.